<\/p>\nAt present, the most widely used aluminum alloy casting production is sodium salt modifier, which consists of halogen salts of sodium and potassium. This type of aluminum alloy modifier is reliable and stable. In the composition of the modifying agent, NaF can play a modifying role. After contact with the aluminum liquid, the following reaction occurs: 3NaF+Al\u2192AlF3+3Na, the sodium produced by the reaction enters the aluminum liquid, which plays a metamorphic role. Because NaF has a high melting point (992\u00b0C), in order to reduce the metamorphic temperature and reduce the absorption and oxidation of aluminum liquid at high temperatures, NaCl and KCl are added to the metamorphic agent. Adding a certain amount of ternary modifier composed of NaCl and KCl, its melting point is below 800\u2103. At a general modification temperature, it is in a molten state, which is conducive to the modification and improves the modification rate and effect.<\/p>\n
In addition, the aluminum alloy modifier in the molten state easily forms a continuous covering layer on the liquid surface, which improves the covering effect of the modifier. For this reason, NaCl and KCl are also called fluxes.<\/p>\n
Some modifiers are added with a certain amount of cryolite (Na3AlF6). This modifier has the effects of modification, refining, and covering. It is generally called a “universal modifier”. This modifier is often used when casting important castings or when the metallurgical quality of the aluminum liquid is high.<\/p>\n
In production, the modification process is usually carried out after refining and before pouring. The modification temperature should be slightly higher than the pouring temperature, and the melting point of the modification agent is preferably between the modification temperature and the pouring temperature. In this way, the modifier is in a liquid state when it is modified, and it can be poured after the modification, so as to avoid the failure of the modification due to the long parking time. In addition, after the modification process is completed, the modified slag has become a very thick solid, which is easy to peel off, so that the residual flux is not poured into the mold to form flux-containing slag.<\/p>\n
<\/p>\n
When selecting a modifier, the melting point and modification temperature of the modifier are generally determined according to the required pouring temperature. Then you can select the appropriate modifier component according to the melting point of the aluminum alloy modifier.<\/p>\n