Erimi\u015f al\u00fcminyumun gaz giderme ar\u0131tmas\u0131n\u0131n temel amac\u0131, erimi\u015f metalde \u00e7\u00f6z\u00fcnm\u00fc\u015f gaz\u0131 uzakla\u015ft\u0131rmakt\u0131r.<\/p>\n
Al\u00fcminyum ala\u015f\u0131mlar\u0131n\u0131n \u0131s\u0131t\u0131lmas\u0131 ve eritilmesi s\u00fcrecinde, hem kat\u0131 hem de s\u0131v\u0131 metallerin H2, O2 ve di\u011fer gazlar\u0131 emme konusunda belirli bir yetene\u011fi vard\u0131r. Metallerin bu \u00f6zelli\u011fine \u201cgetterleme\u201d denir ve bu, metallerin \u00f6nemli eritme \u00f6zelliklerinden biridir. Uygulamada g\u00f6r\u00fcld\u00fc\u011f\u00fc \u00fczere, metalde adsorpsiyon, \u00e7\u00f6z\u00fcnme ve birle\u015fim halinde bulunan gazlar\u0131n, metalin ve ala\u015f\u0131m\u0131n \u00f6zellikleri ile k\u00fcl\u00e7enin kalitesi \u00fczerinde olumsuz bir etkisi vard\u0131r.<\/p>\n
Ala\u015f\u0131mda \u00e7\u00f6z\u00fcnm\u00fc\u015f hidrojen, sac ve \u015feritlerdeki g\u00f6zeneklilik, kabarma ve tabaka ayr\u0131lmas\u0131n\u0131n yan\u0131 s\u0131ra malzemenin hidrojen k\u0131r\u0131lganl\u0131\u011f\u0131n\u0131n da ba\u015fl\u0131ca nedenidir. Malzemeye oksijen, azot ve bunlar\u0131n bile\u015fiklerinin kar\u0131\u015fmas\u0131, malzemenin i\u015flenebilirlik ve mekanik \u00f6zelliklerini bozar. Bu nedenle, eritme i\u015fleminin bir di\u011fer temel g\u00f6revi, erimi\u015f metalde \u00e7\u00f6z\u00fcnm\u00fc\u015f gaz\u0131 gidermektir. Gaz giderme ar\u0131tma y\u00f6ntemini anlamak ve bu konuda uzmanla\u015fmak, metalin gaz emilimini azaltma ve gaz giderme s\u00fcrecini form\u00fcle etmenin anahtar\u0131d\u0131r. Bu, al\u00fcminyum eriyi\u011finin kalitesini iyile\u015ftirmek ve standartlara uygun k\u00fcl\u00e7eler elde etmek a\u00e7\u0131s\u0131ndan b\u00fcy\u00fck \u00f6nem ta\u015f\u0131maktad\u0131r.<\/p>\n
Erimi\u015f al\u00fcminyumun gazdan ar\u0131nd\u0131r\u0131lmas\u0131 ve ar\u0131t\u0131lmas\u0131 i\u00e7in \u00fc\u00e7 y\u00f6ntem vard\u0131r: Birincisi, gaz atomlar\u0131n\u0131n metalin y\u00fczeyine yay\u0131lmas\u0131 ve ard\u0131ndan adsorpsiyon durumundan ka\u00e7mas\u0131d\u0131r; ikincisi, metal eriyikinden kabarc\u0131klar \u015feklinde uzakla\u015ft\u0131r\u0131lmas\u0131d\u0131r; \u00fc\u00e7\u00fcnc\u00fcs\u00fc ise metale eklenen elementlerle bile\u015fikler olu\u015fturmas\u0131d\u0131r. Bu bile\u015fikler, metalik olmayan kal\u0131nt\u0131lar \u015feklinde d\u0131\u015far\u0131 at\u0131l\u0131r. Bu bile\u015fiklerin \u00e7o\u011fu, metal k\u00fcl\u00e7esinde g\u00f6zenekler olu\u015fturmaz.<\/p>\n